This thesis addresses elementary dislocation processes occurring in single-crystalline alloys based on Fe-Al, and investigates correspondences between dislocation distribution inside crystals characterized by transmission electron microscopy (TEM) and surface patterns observed using atomic force microscopy (AFM). Fe-Al alloys with different degrees of ordering were prepared and deformed in compression at ambient temperature in-situ inside the AFM device. The evolution of slip line structures was captured in the sequences of AFM images and wavy slip bands, while cross slip at the tip of the slip band and homogeneous fine slip lines were also identified. Further, the thesis develops a technique for constructing 3D representations of dislocations observed by TEM without the prohibitive difficulties of tomography, and creates 3D models of dislocation structures. Generally speaking, the thesis finds good agreement between AFM and TEM observations, confirming the value of AFM as a relevant tool for studying dislocations.
Subscribe to:
Post Comments (Atom)
The Colt 1911 Pistol (Osprey Weapon 9)
Download The Colt 1911 Pistol (Osprey Weapon 9) First used in combat during the Punitive Expedition into Me...
-
Download Invision Power Board 2: A User Guide. This book is your guide to configuring, managing and maintai...
-
Download Drawdown: The Most Comprehensive Plan Ever Proposed To Reverse Global Warming The 100 most substan...
-
Download The Grant Cardone Rebuttal Manual 200+ Page Rebuttal Manual. Learn to handle any objection with th...
No comments:
Post a Comment